Retention strength of monolithic zirconia crowns cemented with different primer-cement systems

Background The purpose of this in vitro study was to assess the influence of different cement systems with different ceramic primers on the retention strength of zirconia crowns. Methods Thirty extracted molars were prepared with flat occlusal surfaces, 20 degrees taper, and 3 mm axial wall height. A zirconia crown with an occlusal bar was fabricated for each tooth. All specimens were divided (n = 10) into; Group M: Multilink Speed/Monobond N, Group P: Panavia V5/Clearfil Ceramic Primer Plus, Group D: Duo-Link universal/Z-Prime Plus. The intaglio surfaces of crowns were air-abraded using 50 µm alumina at 2.5 bar for 10 s. Then each crown was cemented onto its corresponding tooth. All specimens were thermocycled for 10,000 cycles between 5 and 55 °C. Each crown was subjected to gradually increasing vertical load along the path of insertion through hooks engaging the occlusal bar using a universal testing machine until failure. The force at dislodgment was recorded and retention strength was calculated for each specimen. The failure modes were recorded for each specimen. The data were statistically analyzed using one way ANOVA test followed by Tukey HSD test (α = .05). Results Group D showed lowest strength (1.42 ± 0.23 MPa) and differed significantly (P < .001) from Group M (2.71 ± 0.45 MPa) and Group P (2.47 ± 0.41 MPa). There was no significant difference (P = .34) between Group M and Group P. The failure modes for Groups M and Group P were mainly cohesive, while Group D showed adhesive failure. Conclusions The retention strength of zirconia crowns was improved with Multilink Speed and Panavia V5 cement systems, while the use of the Duo-Link Universal cement system only showed half of those retention strength values.


Background
The use of monolithic zirconia restorations has gained popularity because of its good biocompatibility, improved esthetic quality, high strength and fracture toughness, optical properties, and the overcoming of veneer cracking or chipping problems with veneered zirconia and fabrication of the restoration from presintered homogenous blocks with CAD/CAM technique that contributes to limited amounts of manufacturing defects and reduced production time and cost [1][2][3][4][5]. In contrast to lithium disilicate, zirconium oxide has high surface stability and resistance to etching with hydrofluoric acid due to the lack of a glassy matrix and the inability to benefit from silane due to the lack of silicon dioxide content [6][7][8][9]. Zirconia restorations can be cemented conventionally, but the bond of zirconia to the tooth could improve the marginal seal, retention and, fracture resistance of the restored tooth and transferring of stress from ceramic to the tooth which will prevent crack initiation [10][11][12][13][14][15]. The improvement of the bonding between resin cement and Open Access *Correspondence: mghazy@mans.edu.eg Department of Fixed Prosthodontics, Faculty of Dentistry, Mansoura University, Box 35516, Mansoura, Dkahlia, Egypt zirconia can be achieved with various techniques such as airborne-particle abrasion with alumina, silica deposition methods, plasma spraying, selective infiltration etching, and application of MDP (methacryloyloxydecyl dihydrogen phosphate) primer [8,16,17]. Airborne-particle abrasion with 50 μm alumina particles combined with the use of an MDP-containing primer followed by a resin cement has been advocated for zirconia bonding [10,18]. The advantages of airborne particle abrasion with aluminum oxide particles are the roughening of the zirconia which leads to a micromechanical interlocking between resin cement and zirconia as well as an increase in the surface energy and the surface area [19][20][21]. In addition, the advantage of using a primer containing MDP offers a chemical bonding between the acidic groups of the monomer and the oxide layer of zirconia [22][23][24][25][26].
The MDP monomer could be incorporated directly into various components of the cement system such as primers, adhesives, and resin cements [27]. The MDP molecule consists of methacrylate group that polymerizes into resin and has a hydrophobic group that resists hydrolysis and degradation through water uptake, and a hydrophilic group that reacts with zirconia [28,29]. Certain ceramic primers contain a phosphate ester group and a methacrylate group and acts as an adhesive promotor that bonds to zirconia resulting in durable bond under clinical conditions [30,31].
The most commonly used laboratory tests to measure bond strength are shear, tensile, microtensile, push out and crown retention tests [32]. The variability in outcomes between these test procedures makes it difficult to establish a correlation between laboratory data and the clinical behavior of materials tested [33]. The crown retention test is a more clinically related test for experimentation of the retention of cemented restoration [34]. In many published studies, the crown retention test has been used to assess the retention strength of cemented zirconia crowns [35][36][37][38].
The purpose of this in vitro investigation was to assess the influence of primer-cement systems with different functional phosphate monomers (Multilink Speed/Monobond N, Panavia V5/Clearfil Ceramic Primer Plus, and Duo-Link universal/Z-Prime Plus) on retention of zirconia crowns. The null hypothesis tested was that the monolithic zirconia crowns would not have similar retentive strength when cemented with different primer-cement systems with different functional phosphate monomers.

Specimen collection
Thirty extracted mandibular second molars with approximate dimensions, free from caries, cracks, or fractures, were collected for the current study. Approval to use human teeth was obtained from the local Research Ethics Committee. The selected teeth were cleaned and stored in a 0.1% thymol solution for 6 months at room temperature. Based on the type of cement system, the teeth were randomly assigned into (n = 10): Group M; Multilink Speed/Monobond N, Group P; Panavia V5/Clearfil Ceramic Primer Plus, Group D; Duo-Link universal/Z-Prime Plus (Table 1).

Tooth preparation
The root of each tooth was fixed in an auto polymerizing resin material (Kemapoxy 150, CMB International, Egypt). A silicon index (Presigume Putty, President Dental, Germany) was then fabricated for each tooth. Tooth preparation was carried out with a straight handpiece (Strong Traus AT-II, Saeshin Precision Co., Korea) and a paralleling device (Marathon-103 surveyor, Saeyang Co., Korea). All preparations were done by a single operator (M.S). The height of the preparation was 3 mm with a flat occlusal surface and axial surfaces were prepared with a tapered diamond (TR-14-198/022, Mani Inc., Japan) to create 10 degrees taper with a 0.5 mm chamfer finish line [37,39,40] (Fig. 1).

Determination of preparation surface area
To determine the surface area, each prepared tooth was scanned (Identica Hyprid, MEDIT Corp, Seoul, Korea). The surface area of each preparation was then calculated from the standard tessellation language (STL) file using three-dimensional computer graphics software (Meshlab software version:2020.09, Istituto di Scienzae Tecnologie dell'Informazione, Italy) ( Fig. 2).

Fabrication of the restoration
After each tooth has been scanned, the restoration was designed (collab 2017; Exocad GmbH, Germany) with an occlusal bar (15 mm × 3.5 mm × 3.5 mm) to enable vertical attachment of the cemented crown during the retention testing (Fig. 3). The bar was used to provide attachment for vertically lifting the cemented crown off the prepared tooth. All restorations were milled from a zirconia block (Katana zirconia STML A2, T14, Kuraray Dental, Japan) using a milling machine (Cori Tec 250i, imes-icore GmbH, Germany). All milled crowns were then sintered (Tabeo-100, Mihm-Vogt, Germany) following the instructions of the manufacturer.

Cementation
The intaglio surfaces of all crowns were airborne particle abraded using 50 μm aluminum oxide particles (

Aging
All specimens were thermocycled (SD Mechatronic thermocycler THE-1100, SD Mechatronics, Westerham, Germany) for 10,000 cycles between 5 and 55 °C each with a dwell time of 30 s.

Retention test
Each specimen was secured with tightening screws to the lower fixed part of a universal testing machine (Instron, 2519-104, 3345, Canton, MA, USA). The crown was attached to the upper movable part with a custommade loop wire that was hooked around the occlusal bar (Fig. 4). The cemented crowns were submitted to a rising vertical load along the path of insertion at a crosshead speed of 0.5 mm/min till failure occur. The force at dislodgment was noted in Newton (N) and the retention strength was calculated and recorded in Mega Pascal (MPa).

Failure analysis
The mode of failure was classified according to cement location after removal of the crown: Class 1; adhesive failure (cement mainly remains on the prepared tooth surface), Class 2; mixed adhesive and cohesive failure (cement on crown and tooth), Class 3; adhesive failure  (cement mainly the on crown), Class 4: cohesive failure (zirconia crown fracture), or Class 5; cohesive failure (tooth fracture) [35]. Selected specimens were inspected using a scanning electron microscope (JSM-6510LV, JEOl Ltd., Tokyo, Japan).

Statistical analysis
The data were resolved using a statistical software program (SPSS v26.0; SPSS Inc). Normality of the data was tested using the Shapiro-Wilk test. A one-way ANOVA test was utilized to identify the presence of a significant difference between the mean strength values of the studied groups, followed by the Tukey HSD test (α = 0.05). Differences among failure mode patterns were identified using the Monte Carlo test.

Results
The maximum retention load, preparation surface area, and crown retention strength values are displayed in One-way ANOVA test showed significant differences in the maximum retention load (F = 27.68, P < 0.001) and strength (F = 33.34, P < 0.001) among the test groups ( Table 2). The Post-hoc test showed that the retention strength of crowns cemented using Duo-Link cement system were significantly lower (P < 0.001) than those cemented using either Multilink or Panavia V5 cement systems. However, there was no significant difference between Group M and Group P (P = 0.34). There was no significant difference in prepared surface areas among the different groups (F = 0.37, P = 0.68).
The frequency of failure modes between study groups are presented in Table 3. The Monte Carlo test showed a significant difference in failure modes (P < 0.001) among the test groups. The predominant failure mode observed was cohesive within Groups M and Group P, while Group D had mainly adhesive failures (Fig. 3).

Discussion
The results of the present study favor acceptance of the null hypothesis, since the retention strength of zirconia crowns zirconia was significantly affected by the type of cement system with different primers.
In the current study, monolithic zirconia was used because of its high flexural strength and fracture toughness and can be used in thickness as low as 0.5 mm [3][4][5]. In contrast to glass ceramic, however, zirconia is not susceptible to etching because it does not contain a glassy matrix which rules out the use of conventional adhesive procedures [6]. One self adhesive resin cement (Multilink Speed) and two self etch adhesive resin cements (Panavia V5 and Duo-Link universal) were selected for the current study. These cements were chosen for their good physical properties and ease of use [7]. The resin cements containing the MDP monomer can lead to a high bond strength to zirconia due because of reaction between the hydroxyl groups of the zirconia surface and the phosphate ester group of the MDP molecules [11,15,17]. The acidic
The crown retention test was used in this study because it simulates clinical use for testing the retention strength of resin cements and the results are reproducible and less variable [32,34,37]. In this study, compromised preparation criteria was performed for the retention test with a flat occlusal surface, 3 mm preparation height, and a high angle of convergence 20 degrees [32,39]. These criteria can help ensure that crowns are depend primarily on cementation rather than the geometry of tooth preparation and avoid tooth fracture which is an unwanted situation [39]. The aim of retention test was to evaluate the retentive quality of the resin cement rather than the cohesive strength of the tooth [32].
The outcomes of the present investigation showed that the highest retention strength value was recorded for Group M and the least retention strength value was recorded for Group D. This finding is supported by previous studies in which MDP containing primers with air abraded zirconia surfaces were used to enhance physicochemical interaction between zirconia and the resin cement [6,[23][24][25]30]. In addition to a functional phosphoric acid group in the MDP molecule, the ceramic primer (Monobond N) also contains methacrylate monomers, which together can form a stable bond that is resistant to hydrolysis and offers a strong and durable bond with zirconium oxide [15,20]. Amaral et al. [29], showed higher bond strengths when using the Monobond Plus ceramic primer.
There was no significant difference in retention strength between Groups M and Group P in this investigation. The Panavia V5 tooth primer contains co-initiators that initiate the conversion with an initiator of the resin cement on contact without light curing, which leads to good polymerization of resin cement paste and offers superior dentin bonding performance [43]. Furthermore, owing of its low water sorption, Panavia V5 resin cement is less influenced by thermal cycling [13]. Furthermore, Clearfil Ceramic Primer Plus contains MDP and a silane intended to increase chemical bonding to air abraded zirconia [14]. A previous study showed that treating zirconia with Clearfil Ceramic Primer or Monobond Plus gave the best results. In addition, other studies have found higher a bond strength for Panavia V5 resin cement [9,21].
Group D had the lowest retention strength, which could be elucidated by the fact that Duo-link resin cement is a Bis-GMA based cement, and Bis-GMA based resin cement has been shown to have lower adhesive strength to zirconia than adhesive phosphate monomerbased resin cements [39]. Also, Z-prime plus includes two adhesive monomers (carboxylate and MDP), and the presence of carboxylic acid monomers can weaken the bond between this primer and methacrylate groups found in this resin cement [26]. It was assumed that the lower bond strength of Duo-link and Z Prime plus is due to chemical differences in the base monomers or solvents of the primers, differences in the primer initiation systems, or to variations in the concentration of MDP [17]. Furthermore, dentin bonding agent can be classified as total etch, one step self etch and self etching primer/ adhesive system, also may be HEMA based or HEMA free and All Bond Universal is a HEMA based dentin bonding agent which may be susceptible to water uptake from dentinal tubules and permeate polymerized hydrophilic bonding agent as a result it may interfere with subsequent coupling with Duo-link Universal [44].
The mode of failure for Group M in this investigation was largely cohesive. The cohesive failures were most often observed within the resin cement in Group P. Such failure indicates high bond strength, as it is assumed that the bond strength to the crown and dentin surfaces is higher than the tensile strength of the cement. Halabi et al. [14] showed a predominantly cohesive failure within the Panavia V5 resin cement compared to adhesive failures at the interface of resin and dentin of Estecem II and Rely X Ultimate. The adhesive failures were observed in Group D. This result is in line with another study that compares the adhesive failure mode of Duo-Link Universal to the cohesive failure in Rely X Unicem and Panavia F2.0 [39].
Scanning electron microscope examination of the zirconia surfaces for Groups M and Group P showed a preponderance of residual resin cement that remained on the zirconia surfaces [14,15]. Specimens from Group D showed a large proportion of resin cement that remained on tooth surfaces [39] (Fig. 5).
Limitations of this in vitro study were the lack of load aging, various preparation heights, different convergence angles, and different crown thicknesses. The current study used thermal cycling to mimic the stresses of an intraoral environment but used water baths instead of artificial saliva. Also, only one type of zirconia was used and the results cannot be generalized to other zirconia materials.

Conclusions
Within the limitations of this in vitro study, it was concluded that;